Hot Dipped Seamless Galvanized Steel Pipe ASTM A53 Material Zinc
Coated Surface
1. Galvanized Pipe
Galvanized pipe ordered under ASTM A53 Specification shall be
coated with zinc inside and outside by the hot-dip process. The
zinc used for coating shall be any grade of zinc conforming to
Specification B6.
Weight (Mass) per Unit Area of Coating Test- The weight (mass) per
unit area of zinc coating shall be determined by stripping tests in
accordance with Test Method A90/A90M.
Test Specimens-Test specimens for determination of weight (mass)
per unit area of coating shall be taken, one from each end of one
length of galvanized pipe selected at random from each lot of 500
lengths, or fraction thereof, of each size.
2. Standards:
ASTM A53 Standard Specification for Pipe, Steel, Black and
Hot-Dipped, Zinc-Coated, Welded and Seamless
3. Application:
Steam, water, gas and air lines;
Refinery, Boiler and Mechanical equipment manufacture;
Structure construction; drilling, ship building and etc.
4. Ordering Information
Quantity (feet, meters, or number of lengths),
Grade (A or B),
Finish (black or galvanized)
Size (either nominal NPS/DN and weight class or schedule number, or
both; or outside diameter and wall thickness),
Length (specific or random),
End finish (plain end or threaded)
Close coiling, if desired
NDE test for seamless pipe
Marking
Special requirements
5. Chemical Requirements
| Chemical Requirements |
| Grade | Composition, % |
| Carbon (C) | Manganese (Mn) | Phosphorus (P) | Sulfur (S) | Copper (Cu) | Nickel (Ni) | Chromium (Cr) | Molybdenum (Mo) | Vanadium (V) |
| max | max | max | max | max | max | max | max |
| Grade A | 0.25 | 0.95 | 0.05 | 0.045 | 0.40 | 0.40 | 0.40 | 0.15 | 0.08 |
| Grade B | 0.30 | 1.20 | 0.05 | 0.045 | 0.40 | 0.40 | 0.40 | 0.15 | 0.08 |
6. Mechanical Properties
| Mechanical Properties |
| Grade |
| | A | B |
| Tensile strength, min: | | |
| ksi | 48 | 60 |
| Mpa | 330 | 415 |
| Yield strength, min: | | |
| ksi | 30 | 35 |
| MPa | 205 | 240 |
7. Test Methods
The test specimens and the tests shall conform to those described
in the latest issue of Test Methods and Definitions A370.
Each longitudinal tension test specimen shall be taken from a pipe
end and shall not be flattened between the gage marks.
Test specimens for bend tests and flattening test shall be taken
from pipe. Test specimens for flattening tests shall be smooth on
the ends and free from burrs.
Tests shall be conducted at room temperature.
8. Available Size Range
| OD | Thickness |
| mm | inch | mm | SCH |
| 88.9~1422 | 3''~ 56'' | 2.11~140 | ≥SCH10 |